The objective of this study is to prepare a cellulose paper that was impregnated with silver nanoparticles (AgNPs) for the purpose of water
purification (disinfection and filtration). AgNP papers were prepared by chemical reduction of silver nitrate (AgNO3) with various
concentrations (0.005 M, 0.015 M, 0.03 M, and 0.05 M) using sodium borohydride (NaBH4) as a reducing
agent. Two ratios for NaBH4/AgNO3 of 2:1 and 10:1 were used to show the effect of reduction on the formation and removal
efficiencies of AgNPs. AgNP papers were characterized using scanning electron microscopy and transmission electron microscopy. An acid digestion
using HCl acid followed by analyzing the samples in an atomic absorption spectrometer (ASS) was conducted to measure the silver concentration in AgNP
papers. TEM images showed that the silver nanoparticle size in the papers varied from 1.3 to 75 nm.
Water samples, after filtration through AgNP papers, were analyzed using ASS to measure the silver concentration in the effluent water. AgNP paper
antibacterial efficiency ranged from 99 % to 100 % for both reduction ratios. The average silver content in the effluent water for the three
replicates ranged from 0 to 0.082 mgL-1, which meets the United States Environmental Protection Agency (US-EPA) guideline for drinking
water of less than 0.1 mgL-1. Turbidity tests showed that these papers can be usefully used as point-of-use filters as the turbidity
reduced to less than 1 NTU (Nephelometric Turbidity Units).
Introduction
Water is the common medium for many pathogens because it contains several bacteria, viruses, etc. The removal and inactivation of pathogenic
microorganisms are the last steps in the treatment of drinking water (Phong et al., 2009). Although disinfection methods currently used in drinking
water treatment can effectively control microbial pathogens, researches in the past few decades have revealed a dilemma between effective disinfection
and formation of harmful disinfection byproducts (DBPs) (Li et al., 2008). When chlorine comes in contact with natural organic matter (NOM),
carcinogenic compounds such as trihalomethanes (THMs) and haloacetic acids (HAAs) can be formed (Lalley et al., 2014).
Nanotechnology as well as its application is one of the rapidly developing sciences (Hossain et al., 2014). It is an important field of modern research dealing with the design, synthesis, and manipulation of a particle's structure ranging from
approximately 1–100 nm (Korbekandi and Iravani, 2012). Among the most promising nanomaterials with antibacterial properties are metallic
nanoparticles, which exhibit increased chemical activity due to their large surface to volume ratios and crystallographic surface structure (Savage
and Diallo, 2005). Silver nanoparticles have proved to be most effective as they have good antimicrobial efficacy against bacteria, viruses and other
eukaryotic microorganisms (Rai et al., 2009). The investigation of enhanced disinfection through the use of silver nanoparticle (AgNP) surface
immobilization has been continually explored. From silver-doped hydroxyapatite coatings for reduced infection rate of implanted biomedical devices
(Bai et al., 2012) to silver-impregnated ceramic filters for point-of-use treatment in rural Guatemala (Kallman et al., 2011), AgNP-coated surfaces have displayed a wide range of potential applications.
These commonly encountered materials could be beneficial in maintaining bacteria-free water which is being stored or transported. Graphene, activated
carbon and nepheline films have also been studied for AgNP immobilized antibacterial surfaces (Lalley et al., 2014).
Cellulose materials serve as a good material for embedding metal nanoparticles due to their ability for metal ion absorption. Metal cations have an
affinity for anionic carboxylic acid groups in paper; the porosity of the base paper allows microorganisms to come into contact with the biocide, but
attachment to the fiber surfaces limits the level of silver in the effluent water. The large pore size in the paper allows for reasonably rapid flow
by gravity without the need for pressure or suction (Dankovich and Gray, 2011).
The main objective of this study is to prepare disinfection material that has a high antibacterial efficiency, few side effects and can be readily used
for water treatment. This study considers the use of nanotechnology, specifically the use of silver nanoparticles (AgNP) for water disinfection purposes
(inactivating of Escherichia Coli, Staphylococcus aureus, Enterococcus faecalis, Klebsiella pneumoniae and Enterobacter aerogenes).
Materials and methodsSampling
The study area was Shatt Al-Hilla river at Al-Hilla city, Iraq, from which the samples were taken during the period 2018 to 2019; this is because this river is the
main source of water in the city, and we wanted to investigate the ability of AgNP papers to purify this water. Water sample characteristics are presented in
(Table 1). A sample of 500 mL of water was grabbed and kept in precleaned plastic bottles. The samples were analyzed immediately to prevent
any change in their quality that may occur.
Cellulose papers: (a) before being impregnated with AgNPs, (b) during preparation of AgNPs with a NaBH4/AgNO3 ratio of 2:1, and (c) during preparation of AgNPs with a NaBH4/AgNO3 ratio of 10:1.
A 10 cm× 10 cm× 0.8 mm off-white paper, 100 % alpha cellulose, Whatman Gel Blot GB005, was used to
embed silver nanoparticles. AgNP papers were prepared by in situ reduction of AgNO3 with various concentrations (0.005 M,
0.015 M, 0.03 M and 0.05 M) and two reduction ratios of 2:1 and 10:1, to show the effect of increasing the concentration
of the reducing agent on the formation of AgNPs. Each paper was soaked in 40 mL of AgNO3 solution for 30 min; then it was washed
with ethanol for 1 min to remove the excess Ag ions which were not adsorbed by the paper. To form AgNPs, the paper was placed in 40 mL of
NaBH4 solution for 1 h. After that, the paper was soaked in deionized water for 30 min. Then the paper was dried in the oven at
60 ∘C for 2.5 h. Figure 1 shows the papers before and after embedding with AgNPs.
Characterization
The synthesized AgNP papers were characterized by scanning electron microscopy (SEM), type Quanta 450, available at the University of Babylon (College
of Pharmacy) and transmission electron microscopy (TEM) available at Al-Nahrain University (College of Medicine).
Acid digestion
To determine the amount of dissolved silver in the AgNP paper, an acid digestion of the paper was performed, and then the amount
of dissolved silver was analyzed with an atomic absorption spectrometer (AAS, type AA320N) available at the University of Babylon (College of Material
Engineering). Approximately 100 mg of the dried AgNP paper was reacted with 5 mL of nitric acid (HNO3) and 5 mL of
water. The mixture was boiled until the paper was disintegrated. A volume of 5 mL of 30 % hydrogen peroxide (H2O2) was added to the
mixture to assist in the complete oxidation of the organic matter and to release additional metals into the solution. The mixture was boiled again,
left to be cooled, and then filtered through Whatman filter paper (grade 41) with a diameter of 15 cm; it was then diluted by adding 100 mL of
water. The diluted mixture was tested for silver content using an AAS.
Microbiological test
Urinary tract infections (UTIs) chromogenic agar was prepared by suspending 47.5 g of the medium in 1 L of distilled water. The
mixture was mixed well and dissolved by heating with frequent agitation. Then it was boiled for 1 min until complete dissolution. The medium
was sterilized by placing it in an autoclave at 121 ∘C for 15 min; then it was cooled to 45–50 ∘C, mixed
well, dispensed into plates and left to solidify. The dehydrated medium was homogeneous, free-flowing and beige in color.
The samples were cultured using the serial dilutions method: 1 mL of the sample was diluted in 9 mL of distilled water (1:10
dilution). This process repeated until a 1:100000 dilution was reached. A volume of 0.1 mL of each dilution was spread over a medium plate, and then the plates were
incubated at 37 ∘C for 48 h in an incubator (LIB-030M). The colonies were counted by eye and colony-forming units per milliliter were
calculated using the following equation (Hameed et al., 2015):
CFUmL=No. of colonies⋅Dilution factorVolume of the sample plated(mL).
(a) Images obtained from SEM using 2:1NaBH4/AgNO3 ratio. (b) Images obtained from SEM using 10:1NaBH4/AgNO3 ratio. (c) TEM images using 2:1NaBH4/AgNO3 ratio. (d) TEM images using 10:1NaBH4/AgNO3 ratio.
Results and discussionPaper characterization
The AgNP papers were characterized by SEM and TEM. Figure 2 represents the images obtained by SEM to show the presence of AgNPs in paper fibers and
the images obtained by TEM to determine the particle sizes of AgNPs. Table 2 represents the particle sizes of AgNPs obtained by TEM.
TEM images and results presented in Table 2 showed that an excess of sodium borohydride reductant (10:1 ratio of sodium borohydride to silver
nitrate) resulted in more uniform and smaller nanoparticles. This can be due to the increased speed of reduction with the increment in the reducing
agent (Quintero-Quiroz et al., 2019) . These results agree with the findings of the previous studies concerning this subject.
AAS test showing the silver content of each paper.
Silver content (mg Ag g−1) of dried paper AgNO32:110:1concentration,NaBH4/AgNO3NaBH4/AgNO3Mratioratio0.0053.9584.3430.0154.6254.6980.037.0077.9110.057.8678.769Acid digestion
Acid digestion was performed to determine the silver content of the paper. The results were obtained by using AAS (type AA320N). Table 3 shows the
results of the AAS test.
The acid digestion of AgNP papers showed silver content ranging from 3.9 to 8.7 mgAgg-1 (milligram Ag per dry gram of paper). The increase in silver content of the paper correlates with the increase in precursor silver ion concentration of the solution in which
the papers were soaked, prior to reduction (Dankovich and Gray, 2011). For the same concentration of AgNO3, the
NaBH4/AgNO3 ratio of 10:1 resulted in more silver content than the 2:1 ratio. These results agree with the findings of the
previous studies concerning this subject.
The removal efficiency of different types of bacteria with NaBH4/AgNO3 ratio of 2:1: (a)E. coli, (b)Staphylococcus aureus, (c)Enterococcus faecalis, (d)Enterobacter aerogenes and Klebsiella pneumoniae, and (e)Proteus mirabilis.
The removal efficiency of different types of bacteria with NaBH4/AgNO3 ratio of 10:1: (a)E. coli. (b)Staphylococcus aureus. (c)Enterococcus faecalis. (d)Enterobacter aerogenes and Klebsiella pneumoniae. (e)Proteus mirabilis.
Removal efficiencies of bacteria
Figures 3 and 4 show the effect of the silver content in the AgNP paper on the removal efficiency of different types of bacteria with a
NaBH4/AgNO3 ratio of 2:1 and 10:1, respectively.
As shown in Figs. 3 and 4, the minimal inhibitory concentration (MIC), which is the lowest concentration of silver nanoparticles needed to inactivate
the bacteria, for E. coli for all three filtration times was 4.62 mgAgg-1 dry paper for a NaBH4/AgNO3
ratio of 2:1, while for 10:1, the MIC for complete inactivation of E. coli was 4.34 mgAgg-1 dry paper. The MIC for
complete inactivation of Staphylococcus aureus was 7.01 mgAgg-1 dry paper for 2:1 ratio and 4.7 mgAgg-1 dry
paper for 10:1 ratio. The MIC for complete inactivation for Enterococcus faecalis was 4.01 mgAgg-1 dry paper for 2:1 ratio
and 4.7 mgAgg-1 dry paper for 10:1 ratio. The removal efficiency for Enterobacter aerogenes and Klebsiella for all
silver contents and both ratios was 100 %.
It was observed that for all types of bacteria, the NaBH4/AgNO3 ratio of 10:1 resulted in complete inactivation of bacteria in
less silver content than the 2:1 ratio and that the 10:1 ratio resulted in smaller and more uniform AgNPs, which led to better contact
between the AgNPs and the bacteria (Bakhtiari-Sardari et al., 2020). These results agree with the findings of the previous studies concerning this
subject.
Analysis of silver content in the effluent
Due to possible human health effects from silver exposure, the silver content in the effluent water was analyzed by AAS. Table 4 represents the
relationship between the silver content in the paper and silver release in the effluent.
The relationship between the silver content in the papers and silver in the effluent water.
Silver content in the Effluent,mgL-1AgNO32:110:1concentration,NaBH4/AgNO3NaBH4/AgNO3Mratioratio0.005000.015000.030.0210.0430.050.0430.082
Turbidity results before and after filtration through AgNP paper for both reduction ratios.
AgNO3 concentration, M2:1NaBH4/AgNO3 ratio 10:1NaBH4/AgNO3 ratio Turbidity before filtering through papers (NTU)Turbidity after filtering through papers (NTU)Turbidity before filtering through papers (NTU)Turbidity after filtering through papers (NTU)0.00513.50.9213.50.820.01512.10.3312.10.120.0312.10.2212.10.130.0513.50.8713.50.81
As shown in Table 4, the average silver content in the effluent water for the three replicates ranged from 0 to 0.082 mgL-1, which meets
the United States Environmental Protection Agency (US-EPA) guideline for drinking water of less than 0.1 mgL-1 (EPA, 2018). This was due to the stability of silver nanoparticle in the cellulose paper. Sodium
borohydride acts not only as a reducing agent but also as an ion stabilizer, which prevents silver ions from aggregation. Moreover, hydroxyl and ether
groups in the cellulose fiber play an important role in the stabilization of metal nanoparticles (Pinto et al., 2012). These results agree with the
findings of the previous studies concerning this subject.
Turbidity removal
Turbidity tests were conducted using a turbidity meter, SN 10/1467, Germany, available at the University of Babylon (College of Engineering, Environmental
Engineering Department). Table 5 represents the results obtained before and after filtration through AgNP papers.
As shown in Table 5, the cellulose paper acts as a good point-of-use filter as all the turbidities were reduced to an acceptable level. Reducing the
papers with the 10:1NaBH4/AgNO3 ratio reduced the turbidity better than the 2:1NaBH4/AgNO3 ratio.
Conclusions
Sliver nanoparticles used in this work exhibit a broad size distribution with highly reactive facets. It was observed that chemical reduction of
AgNO3 by using NaBH4 as a reducing agent resulted in spherical silver nanoparticles. The ratio for
NaBH4/AgNO3 of 10:1 resulted in smaller sizes of silver nanoparticle and more silver content than the ratio of 2:1 for the
same AgNO3 concentration. AgNP paper provided rapid and effective bactericidal activity as the bacterially contaminated water was filtered
through the paper; this is especially important for Enterococcus faecalis, which is for the first time tested for removal by AgNPs. AgNP papers can be used as
good point-of-use filters.
SAR has done samples and data collection and lab experiments as well as writing and editing the paper. AHA role was supervising the process of data and samples collection and experiments and made the final correction to writing.
Competing interests
The authors declare that they have no conflict of interest.
Acknowledgements
This study was supported by the Department of Environmental Engineering in the University of Babylon. We also appreciate the support of the sanitary lab in the College of Engineering that helped carry out this work.
Review statement
This paper was edited by Luuk Rietveld and reviewed by Mona Soliman and one anonymous referee.
References
Bai, X., Sandukas, S., Appleford, M., Ong, J. L., and Rabiei, A.:
Antibacterial effect and cytotoxicity of Ag-dopedfunctionally graded hydroxyapatite coatings,
J. Biomed. Mater. Res. B,
100B, 553–561, 2012.Bakhtiari-Sardari, A., Mashreghi, M., Eshghi, H., Behnam-Rasouli, F., Lashani, E., and Shahnavaz, B.:
Comparative evaluation of silver nanoparticles biosynthesis by two cold-tolerant Streptomyces strains and their biological activities,
Biotechnol. Lett.,
10.1007/s10529-020-02921-1, in press, 2020.Dankovich, T. A. and Gray, D. G.:
Bactericidal Paper Impregnated with Silver Nanoparticles for Point-of-Use Water Treatment,
Environ. Sci. Technol., 45, 1992–1998,
10.1021/es103302t, 2011.EPA: EPA 822-F-18-001, in: 2018 Edition of the Drinking Water Standards and Health Advisories, Office of Water, US Environmental Protection Agency Washington, DC, 2018.
Hameed, U., Muhammad, A., Jahngeer, A.; and ul Haq, I.:
Determination of Microbial load of Drinking Water from different areas of Lahore,
Biologia (Pakistan),
61, 151–156, 2015.
Hossain, F., Perales-Perez, O. J., Hwang, S., and Román, F.:
Antimicrobial nanomaterials as water disinfectant: applications, limitations and future perspectives,
Sci. Total Environ.,
466–467, 1047–1059, 2014.
Kallman, E. N., Oyanedel-Craver, V. A., and Smith, J. A.:
Ceramic filters impregnated with silver nanoparticles for point-of-use water treatment in rural Guatemala,
J. Environ. Eng.,
137, 407–415, 2011.Korbekandi, H. and Iravani, S.:
Silver Nanoparticles, InTech, Intechopen, 978-953-51-0615-9, 10.5772/34157, 2012.
Lalley, J., Dionysios, D., Varma, R. S., Shankara, S., Yang, D. J., and Nadagouda, M. N.:
Silver-based antibacterial surfaces for drinking water disinfection – an overview,
Curr. Opin. Chem. Eng.,
3, 25–29, 2014.Li, Q., Mahendra, S., Lyon, D. Y., Brunet, L., Liga, M. V., Li, D., and Alvarez, P. J.:
Antimicrobial nanomaterials for water disinfection and microbial control: potential applications and implications,
Water Res., 42, 4591–4602,
10.1016/j.watres.2008.08.015, 2008.Phong, N. T., Thanh, N. K., and Phuong, P. H.:
Fabrication of antibacterial water filter by coating silver nanoparticles on flexible polyurethane foams,
J. Phys. Conf. Ser.,
187, 012079, 10.1088/1742-6596/187/1/012079, 2009.Pinto, R. J. B., Neves, M. C., Pascoal Neto, C., and Trindade, T.:
Composites of Cellulose and Metal Nanoparticles, in: Nanocomposites – New Trends and Developments, edited by: Ebrahimi, F., IntechOpen,
10.5772/50553, 2012.Quintero-Quiroz, C., Acevedo, N., Zapata-Giraldo, J., Botero, L. E., Quintero, J., Zárate-Triviño, D., Saldarriaga, J., and Pérez, V. Z.: Optimization of silver nanoparticle synthesis by chemical reduction and evaluation of its antimicrobial and toxic activity, Biomater. Res., 24, 53–67, 10.1186/s40824-019-0173-y, 2019.
Rai, M., Yadav, A., and Gade, A.:
Silver nanoparticles as a new generation of antimicrobials,
Biotechnol. Adv.,
27, 76–83, 2009.
Savage, N. and Diallo, M. S.:
Nanomaterials and water purification: Opportunities and challenges,
J. Nanopart. Res.,
7, 331–342, 2005.